SUS630 ( 17-4PH ) Cold Rolled Stainless Steel Strip In Coil And Sheet Plate
Material SUS630 ( 17-4PH ) is a martensitic precipitation hardening stainless steel that provides an outstanding
combination of high strength, good corrosion resistance, good mechanical properities at temperatures up to
316℃, good toughness in both base metal and welds, and short time, low temperature heat treatments that
minimize warpage and scaling.
Typical application
17-4PH stainless is widely used in the aerospace, chemical, petrochemical, food processing, paper and
general metalworking industries.
Chemical composition %
| C | Si | Mn | P | S | Cr | Ni | Cu | Nb |
| 0.07 max | 1.00 max | 1.00 max | 0.040 max | 0.030 max | 15.00~17.50 | 3.00~5.00 | 3.00~5.00 | 0.15~0.45 |
Standard Heat Treatments
As supplied from the Mill in Condition A, 17-4 PH Stainless Steel can be heat treated at a variety
of temperatures to develop a wide range of properties. Eight standard heat treatments have been developed.
The following chart outlines the times and temperatures required.
This alloy exhibits useful mechanical properties in Condition A.
Condition A material has been used successfully in numerous applications.
The hardness and tensile properties fall within the range of those for Conditions H 1100 and H 1150.
However, in critical applications, the alloy is used in the precipitation-hardened condition, rather than Condition A.
Heat treating to the hardened condition, especially at the higher end of the temperature range, stress relieves the
structure and may provide more reliable resistance to stress corrosion cracking than in Condition A.
| Property | A | H900 | H925 | H1025 | H1075 | H1100 | H1150 |
| UTS, Mpa | 1276 max. | 1310 min. | 1172 min. | 1069 min. | 1000 min. | 965 min. | 931 min. |
| 0.2% YS, Mpa | 1103 max. | 1172 min. | 1069 min. | 1000 min. | 862 min. | 790 min. | 724 min. |
| Elongation, % in 2'' | 3 min. | 5 min. | 5 min. | 5 min. | 5 min. | 5 min. | 8 min. |
| Hardness, Rockwell | C 38 max. | C40~48 | C38~46 | C35~43 | C31~40 | C31~40 | C28~38 |
Forms of supply
SUS630 ( 17-4PH ) stainless steel strip, coil, sheet and plate
SPECIFICATIONS
AMS 5604 Sheet, Strip and Plate
ASTM A 693 Plate, Sheet and Strip
(Listed as Grade 630-UNS S17400)
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com
Contactpersoon: Mr. Paul
Tel.: 86-510-81812873
Fax: 86-510-81812872